ASA Spanish PVC roof sheet accessories endcap of the main ridge tile

This is XROOF ASA Spanish PVC roof sheet special accessories—Endcap of the main ridge tile, used for the main ridge tile head, with the advantages of anti-corrosion, waterproof, impact resistance, sound insulation, fire resistance, insulation and so on.
BrandXROOF
ModelSpanish 1050
Layers4layers
Color
DeliveryTime10-15 Working days after advance
MOQ
Warranty15 years

INQUIRY

 
Accessories Spanish 1050 PVC Roof Core Advantage
 
^_^
^_^
^_^

ASA Spanish Roof Sheet Specification

Width: 1050mm

Effecived width: 960mm

Length: Customized

Thickness: 2.3mm, 2.5mm, 3.0mm

Application: Residential, Villas, Resorts, Hotels, Government Projects, etc.

 
 ASA Spanish Roof Sheet Accessories Product Detail Image
 

ASA Spanish roof sheet is one of the most popular profiles in the XROOF product line, prized for its simple one-piece design, which exhibits a unique corrugated pattern on the roof surface.

Compared to clay roof tiles, Spanish colonial roof sheet can enhance almost any architectural style.

^_^
^_^

Product Application Range

 

The ASA Spanish PVC roof sheet has been praised for its simple one-piece design, which combines a unique corrugated pattern on the roof while reducing the risk of water leaks by reducing tile overlapping locations.

PVC Spanish roof sheet is available in custom finishes, matt, glossy and inkjet finishes.
XROOF ASA Spanish PVC roof sheet provides retro European architectural style for any building, and are commonly used in the roofing of self-occupied residences, villas, hotels, resorts and other buildings.

 
Accessories Spanish 1050 Roof Sheet Test Technical Data From SGS
 

NO.

Test item

Test method

Test condition

Test result

1

Xenon-arc

Exposure

ISO 4892-2:2013,ISO 105-A02:1993

Cor2: 2005 and ASTM D2244-11

ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH

18min light and water sparay Filter: Boro/Boro

Exposure period: 500h

 

Greyscale

2-3

 

∆E*ab

3.5

2

Thermal resistance

With reference to ASTM D3045-92(2010) and client’s requirements

150℃.30min

Visible deformation and color fading, but o other visible change.

3

Muriatic acid resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 35%(m/m) HCI(AR)

Method: Immersion method

Temperature: Room temperature

Test time: 48h

No visisble change

4

Sulfuric acid resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 30%(m/m) H2SO4(AR)

Method: Immersion method

Temperature: Room temperature

Test time: 48h

No visisble change

5

Alikali resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 40% (m/m) NaOH(AR)

Method: Immersion method

Temperature: Room temperature

Test time: 48h

No visible change.

6

Density

ISO 1183-1:2012     Method A

Abosolute alcohol, 23±0.5℃

1.799g/cm3

7

Flexural strength

ISO 178:2010/Amd.1:2013

Method A

Specimen：100x10.96x3.12mm

Testing speed: 1mm/min

Span: 50mm

41.3MPa

8

Flexural modulus

4520MPa

9

Charpy unnotched impact strength

ISO 179-1: 2010

Specimen: ISO 179-1/1Eu

Specimen thickness:3.13mm

The capcaity of the pendulum: 5J

Impact speed: 2.90m/s

Span: 62mm

 

38Kj/M2

C(complete break)

10

Vicat softening temperature

ISO 306:2004 Method B50

Specimen thickness: 3.01mm

Rate of temperature: 50℃/h

77.3℃

11

Tensile strength

ISO 527-1:2012 and ISO 527-2:2012

Specimen: Type 1B

Specimen thickness:3.05mm

Testing speed: 5mm/min

Grip separation:115mm

20.3MPa

12

Nominal tensile strain at break

13%

13

Impact resistance

GB/T 8814-2004 Section 5.7 and 6.7

Precondition:-10℃，1h→

Take out and do test within 10s.

Specimen thickness:3.02mm

Geometry: H.25

Strike weight: 1.0kg

Span: 200mm

Number of specimens tested:10

Number of spcimen breakage:0

14

Dimensional change

With reference to ASTM D1204-08 and client’s requirement

Condition: 100℃，60min→

23±2℃，50±5%RH,1h

Specimen: 25x25cm

Medium:Talcum powder

X

drection

-0.7%

Y

direction

-1.3%

15

Oxygen Index

ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005

Specimen: Type III

Specimen thickness: 3.2mm

Ignition procedure: Method A

 

32.8%

16

Horizontal burning test

UL 94-2013 Section 7

Specimen: 126x13.4x3.0mm

Conditioning: 23±2℃

50±5%RH,48h

HB

17

20mm Vertiacal burning test

UL 94-2013 Section 8

Specimen: 126x13.4x3.0mm

V-1

18

Burning test

DIN 4102-1:1998-05

See appendix1

The sample tested met the requirements of class B2